本期将带您了解静电粉末喷涂工艺及pg电子娱乐平台铝业新引入设备——立式喷涂

广东pg电子娱乐平台铝业

立式喷涂设备

What is the Powder Coating for aluminium profiles?

Powder coating is a dry surface treatment procedure. After the fine pigment particles are electrostatically treated, they are sprayed on the product to form a coating, which is solidified by a curing oven to form a solid coating. Nowadays, most of the coloured aluminium profiles on the market are achieved by powder coating. The coating thickness can reach 40~120 μm.

什么是铝型材粉末喷涂？

粉末喷涂是一种干燥的表面处理程序。将细颜料颗粒静电处理后，将它们喷在产物上以形成涂层，该涂层被固化的烤箱固化以形成固体涂层。

如今，市场上的大多数彩色的铝型材都是通过粉末涂料来实现的。涂层厚度可以达到40〜120μm。

What are the advantages of Powder Coating for aluminium profiles?

1) The surface is beautiful, durable, scratch-resistant, chemically resistant to attack, and UV-resistant;

2) Environmental protection, no waste liquid discharge;

3) Perfect corner coverage;

4) Uniform colour and wide range of spray colours;

5) The thickness is easy to control and thus is widely used.

铝型材粉末喷涂的优势：

1、表面美观、耐用、耐刮擦、耐化学侵蚀、耐紫外线；

2、环保，无废液排放；

3、完美角落覆盖；

4、颜色均匀，喷涂颜色范围广泛；

5、厚度易于控制，因此被广泛应用。

外网资料拓展：

粉末涂料和涂层始于20世纪30年代。最初采用的是将聚乙烯粉末通过火焰喷涂的方式涂在金属表面上，这是粉末涂料的开始。直到20世纪50年代，在德国发明了发明性的粉末床涂覆工艺后，粉末涂料和涂层工艺得到了极大的发展。

而中国开始比较晚。1989年，江苏常州华艺铝型材厂引进了美国 Nordson 粉末涂装设备，这是中国第一家铝粉末涂装。随着经济改革和开放，粉末涂料技术在中国得到了大力发展。初期采用的是横向生产线。但随着经济技术的发展，意大利和日本率先引进立式喷涂生产线并开始广泛应用。立式粉末涂层生产线已经发展成为成熟的产品，从预处理、干燥到粉末涂层的均匀性，再到固化效果，均已达到国外先进水平，由于立式线的占地面积小，操作人员数量少，喷涂的均匀性和固化层的效果均达到完美的结果。

操作流程

粉末喷涂工艺步骤：上架——酸洗——水洗——铬化——水洗——烘干——下架——上架——喷涂——固化——成品包装

水洗：指对铝型材进行预处理前，先洗去附着于型材表面的杂质油脂等，同时在表面形成水膜，避免与氧气接触；

铬化：铬酸盐处理，行业内称“铬化”，该工艺影响后续型材表面附着力和耐腐蚀力；烘干：避免后续漆膜出现气泡、脱落等现象固化：粉末融化后，自流平形成永久性膜。